| Welcome to 3T! Please take the time to register and join in on the friendly,knowledgeable watch talk.Please note that not all registrations will receive an immediate activation e-mail.Those who do not receive an immediate notification will be activated manually within 48hrs. by an admin. without an e-mail activation url sent to you,you may then sign in using your username and password,if you feel there is a problem please e-mail us at timetechtalk@hotmail.com and include your name and username and we activate your account.Thank You! |
| Moderated by: 3T | ||
| Author | Post | |||||||||
|---|---|---|---|---|---|---|---|---|---|---|
|
EricAldovino Guest
|
Really thinking of picking up a Ti Samurai this week... Anyone know if Ti is more likely to ding easily? |
|||||||||
|
oagaspar Site Founder 
|
Ti is about 40% stronger than SS but any metal can be Dinged....the objective is not to "Ding":D:D I bought a Ti Sammie that was dinged(and advertised that way) at a much lower cost to me so Yes Ti can be dingedhand6.gif I happen to like the substantial less weight of Ti for a daily wearerwatch2.gif |
|||||||||
|
watchguru 3T WIS 
|
my issue with titanium is not about dings, but more about surface scuffing... i find that small scuff marks looks much more pronounced on titanium watches than SS... |
|||||||||
|
KenC Admin 
|
watchguru wrote: my issue with titanium is not about dings, but more about surface scuffing... i find that small scuff marks looks much more pronounced on titanium watches than SS... and it is next to impossible to polish them out! |
|||||||||
|
watchguru 3T WIS
|
KenC wrote: watchguru wrote:my issue with titanium is not about dings, but more about surface scuffing... i find that small scuff marks looks much more pronounced on titanium watches than SS... exactly! i have one titanium watch (an ECO-DRIVE diver), but other than that, i stay away from them... |
|||||||||
|
Matt V 3T WIS
|
While Titanium has a larger tactile strength than steel at a lower weight, the surface of typical Titanium alloys is softer and it scratches or dings more easily than most steel alloys. There are variations too, depending on the alloy. I have different watches with different Titanium Aloys (Citizen, Breitling, Omega, Marcello) and they all seem to be just a little different and more or less prone to scratches. Nevertheless, you can brush up Titanium just like steel and within a day or so the surface will develop the oxyde again, leaving it to look just like new. Either way, I love how the Titanium feels on the skin, even on the hottest or coldest days. :) Cheers Matt  |
|||||||||
|
EricAldovino Guest
|
I never mind the surface scratches, my concern is always the ding factor. Well ordered from Higuchi so will be hear in a few days. |
|||||||||
|
IWR222 3T WIS 
|
i dont own a Ti watch,but i have a friend at work (ok ,its just a bloke i work with,billy no mates ) uses a rubber (eraser) not the pencil side but the ink side . He says it works a treat> |
|||||||||
|
Nalu 3T WIS 
|
While Ti is stronger than steel, it is very slightly softer than steel (depending on alloy and surface treatments such as tegimented steel or Duratect). The finish of a watch has a lot to do with how much the scratches show. The advantage of Ti is that scratches oxidise over time and tend to fade into the background as a result. The TiO surface layer exists on all untreated Ti alloys and is very inert - and is responsible for the darker appearance of Ti cases. IME, brushed Ti can be 'repaired' with a fiberglass brush and in days to weeks the repair will be nearly invisible. In this way, the advantages of Ti for a dive watch case (doesn't corrode, hypoallergenic, strong, light, etc.) outweigh the disadvantages. |
|||||||||
|
e.avery 3T WIS 
|
With out getting to tech, there are manufacturing processes that increase the hardness of the surface on the higher end watches, it is not just the alloy. The alloy is a major part but Ventura, Sinn, Breitling, and others process there Ti watches in order to increase the abrasion resistance. Part of the strength of Ti is the malleability and the resistance to things such as brittle fracture, and fatigue. Aerospace or Defense grade alloys of Ti used in other industry's are not typically processed in these ways, due to the lower ability of the metal to deform, thus increasing the brittleness of metal. |
|||||||||
|
EricAldovino Guest
|
Funny, I actually owned a Titanium watch before...I forgot. I had the Junkers mechanical I picked up from marc 2 yrs ago. I like Titanium! I miss that watch. Attachment: 6432-2.jpg (Downloaded 34 times) Last edited on Fri Jun 1st, 2007 02:24 pm by |
|||||||||